Preparation of α-cordierite through mechanochemical activation of MgO–Al2O3–SiO2 ternary system

Samples of the ternary system MgO–Al₂O₃–SiO₂ with stoichiometric composition in relation to α-cordierite (Mg₂A_l4Si₅O₁₈), consisting of 22.2 mol% MgO, 22.2 mol% Al₂O₃, and 55.6 mol% SiO₂, were activated in a low energy mill with a constant speed of 100 rpm, in an aqueous medium. The precursors used were corundum (Al₂O₃), silica gel HF254 type 60 (SiO₂), and periclase (MgO). The objective of the present study was to evaluate the effect of mechanochemical activation on the solid-state synthesis of α-cordierite, using a low energy ball mill. Another objective was to shed light on the effect of mechanochemical activation on the steps of α-cordierite formation. For this end several grinding conditions were evaluated, varying the time and mass ratio of precursors/grinding elements, as well as calcination at different temperatures between 950 °C and 1350 °C for 2 h. The samples were analyzed for the determination of the formed phases by Infrared (IR) and X-ray Diffraction (XRD). The phases identified in uncalcined samples were brucite (Mg(OH)₂), forsterite (Mg₂SiO₄), enstatite (MgSiO₃), spinel (MgAl₂O₃), amorphous silica (SiO₂), corundum (α-Al₂O₃), and zirconia (monoclinic and tetragonal ZrO₂). The lowest temperature corresponding to the formation of α-cordierite (α-Mg₂Al₄Si₅O₁₈) was 1150 °C and a considerable amount of this phase (16.2%) was observed at this temperature, for the sample with the higher mechanochemical activation. In a solid-state reaction, α-cordierite is normally obtained at around 1400 °C, therefore, the formation of this phase at 1150 °C confirms that the mechanochemical activation method, using a low-cost ball mill, is efficient in reducing the solid-state reaction temperature.     

罩式退火温度对高强IF钢组织及性能的影响

为研究不同退火温度下高强IF钢的组织性能及织构的变化规律,采用温箱式电阻炉加热模拟罩式退火工艺,研究了不同退火温度下高强IF钢210P1冷轧板力学性能;对不同退火温度钢板的r90进行了统计并对其进行显微组织观察;采用X射线衍射仪及热场发射扫描电镜对不同退火温度的罩式退火成品板进行了织构分析。结果表明,在高强IF钢210P1冷轧板的罩式退火过程中,提高退火温度将使晶粒明显长大。随着退火温度的升高,屈服强度及抗拉强度下降,伸长率升高,n值略有上升,板材横向r值增加较明显,有利织构{111}取向密度增加,不利织构{100}取向密度降低。     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

风机主轴锻件锻后热处理工艺优化

通过对42CrMo4风机主轴结构尺寸、性能要求、材质特点等方面进行分析,对原有锻后热处理工艺进行优化,制定出既能达到锻后热处理效果又经济节能的工艺参数。     

木片筛余物高得率半化学法清洁制浆技术研究

以太阳纸业备料车间木片筛选碎料（筛余物）为原料，对其烧碱法半化学制浆的实验室工艺和生产试验进行了研究。结果表明，筛余物采用半化学法制浆可获得较高得率和环压强度的纸浆，且用碱量对纸浆性能有显著影响。相对8%NaOH （相对于绝干原料）化学预处理，采用14%NaOH化学预处理结合两段浆浓22%的高浓磨浆工艺，所制半化学浆抄造浆张的裂断长和环压指数分别达2.89 km和9.76 N·m/g，是前者的1.9倍和1.2倍，而且优于现用国内OCC废纸浆抄造浆张；生产试验得到的浆张性能指标与实验室相吻合，其中紧度和环压强度分别达到GB/T 13023—2008瓦楞芯（原）纸AA级和A级优等品要求。     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

Interfacial Crystallization of Diacylglycerols Rich in Medium‐ and Long‐Chain Fatty Acids in Water‐in‐Oil Emulsions

The effects of diacylglycerols rich in medium‐ and long‐chain fatty acids (MLCD) on the crystallization of hydrogenated palm oil (HPO) and formation of 10% water‐in‐oil (W/O) emulsion are studied, and compared with the common surfactants monostearoylglycerol (MSG) and polyglycerol polyricinoleate (PGPR). Polarized light microscopy reveals that emulsions made with MLCD form crystals around dispersed water droplets and promotes HPO crystallization at the oil‐water interface. Similar behavior is also observed in MSG‐stabilized emulsions, but is absent from emulsions made with PGPR. The large deformation yield value of the test W/O emulsion is increased four‐fold versus those stabilized via PGPR due to interfacial crystallization of HPO. However, there are no large differences in droplet size, solid fat content (SFC), thermal behavior or polymorphism to account for these substantial changes, implying that the spatial distribution of the HPO crystals within the crystal network is the driving factor responsible for the observed textural differences. MLCD‐covered water droplets act as active fillers and interact with surrounding fat crystals to enhance the rigidity of emulsion. This study provides new insights regarding the use of MLCD in W/O emulsions as template for interfacial crystallization and the possibility of tailoring their large deformation behavior. Practical Applications: MLCD is applied in preparing W/O emulsion. It is found that MLCD forms unique interfacial Pickering crystals around water droplets, which promote the surface‐inactive HPO nucleation at the oil‐water interface. Thus MLCD‐covered water droplets act as active fillers and interact with surrounding fat crystals, which can greatly enhance the rigidity of emulsion. This observation would provide a theoretical reference and practical basis for the application of the MLCD with appreciable nutritional properties in lipid‐rich products such as whipped cream, shortenings margarine, butter and ice cream, so as to substitute hydrogenated oil. MLCD‐stabilized emulsions can also be explored for the development of novel confectionery products, lipsticks, or controlled release matrices.